Vyuma vya pua SAW waya wa kulehemu ER309L na flux Uunganisho wa kulehemu
TEKNOLOJIA YA KUCHOMA
Usiruhusu maswali
Endelea kukusumbua
Arc kutokuwa na utulivu
Ukingo usiopendeza
Spatter nyingi
Mara nyingi hutumiwa kwa kulehemu kwa chuma cha kaboni na chuma cha pua au kwa
kulehemu kwa chuma cha pua cha martensitic na ferritic na ugumu duni
Inaweza pia kutumika katika petrochemical, mimea ya nguvu ya mafuta na
tasnia zingine kama vile chuma cha mpito cha ndani cha ukuta unaoangazia ukuta.
Ripple faini
Kuchomelea 22%Cr-12%Ni chuma cha pua (SUS309S)
Au chuma cha pua na chuma cha kaboni, kulehemu kwa chuma cha aloi ya chini.
Slagging rahisi
Bidhaa Parameter
COMPONET YA KIKEMIKALI:
ALLOY(wt%) | C | Si | Mn | P | S | Ni | Cr | Mo |
GB/T KANUNI | 0.025 | 0.6 | 1.69 | 0.025 | 0.002 | 12.2 | 22.3 | - |
MALI YA MITAMBO:
MALI | Nguvu ya ugani (Mpa) | Kurefusha/% | THAMANI YA IMAPACT J/℃ | Kutu ya intergranular | ||||
GB/T KANUNI | 570 | 35 | ≥60/joto la ndani | Mbinu ya GB/T4334E imepitishwa |
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
MAELEZO YA DIAMETERS(mm) | 2.4 | 3.2 | 4.0 | ||||
Volt | 28-32 | 28-32 | 28-32 | ||||
Amp | 270-360 | 400-550 | 500-650 | ||||
Kasi(mm/min) | 250-320 | 300-420 | 400-480 | ||||
Urefu kavu (mm) | 20-24 | 22-26 | 30-34 |
Msaada wa kiwanda
Bidhaa hiyo inafaa kwa a
mbalimbali ya maombi
TEKNOLOJIA YA KUCHOMA
-
Vifaa vya kulehemu kwa vyombo
Mradi wa LNG wa Canada
-
Nguvu ya Nyuklia ya Shandong CV20
COMPONET YA KIKEMIKALI:
ALLOY(wt%) | C | Si | Mn | P | S | Ni | Cr | Mo |
GB/T KANUNI | 0.025 | 0.6 | 1.69 | 0.025 | 0.002 | 12.2 | 22.3 | - |
MALI YA MITAMBO:
MALI | Nguvu ya ugani (Mpa) | Kurefusha/% | THAMANI YA IMAPACT J/℃ | Kutu ya intergranular | ||||
GB/T KANUNI | 570 | 35 | ≥60/joto la ndani | Mbinu ya GB/T4334E imepitishwa |
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
MAELEZO YA DIAMETERS(mm) | 2.4 | 3.2 | 4.0 | ||||
Volt | 28-32 | 28-32 | 28-32 | ||||
Amp | 270-360 | 400-550 | 500-650 | ||||
Kasi(mm/min) | 250-320 | 300-420 | 400-480 | ||||
Urefu kavu (mm) | 20-24 | 22-26 | 30-34 |