Chuma cha pua Mwongozo Electrode E312-17 ore mashua weld
TEKNOLOJIA YA KUCHOMA
Usiruhusu maswali
Endelea kukusumbua
Arc kutokuwa na utulivu
Ukingo usiopendeza
Spatter nyingi
Inafaa kwa kila aina ya nyenzo za chuma ngumu na ugumu
chuma cha aloi ambacho ni vigumu kulehemu na ni rahisi kupasuka au kuwa na porosity
Acid aina ya awamu mbili chuma cha pua electrode mkono, jet arc,
sehemu kuu ni 29%Cr-9%Ni, inayojulikana kama "electrode zima.
Ripple faini
Uendeshaji mzuri wa kulehemu, arc thabiti, uundaji mzuri,
alika maridadi, Splash kidogo, rahisi slag kuondolewa.
Mipako ina upinzani mzuri wa moto, upinzani mzuri wa porosity, na mali imara ya mitambo ya chuma kilichounganishwa
Slagging rahisi
Bidhaa Parameter
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Nyingine |
| GB/T KANUNI | 0.057 | 1.1 | 0.74 | 0.026 | 0.005 | 9.8 | 28.4 | 0.07 | 0.11 | - |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | THAMANI YA IMAPACT J/℃ | Matibabu ya joto °C*h | ||||
| GB/T KANUNI | 800 | 25 | - | - | ||||
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
| MAELEZO YA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| UMEME (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||
Msaada wa kiwanda
Bidhaa hiyo inafaa kwa a
mbalimbali ya maombi
TEKNOLOJIA YA KUCHOMA
-
mapipa milioni 2.3 ya
SBM Fast4ward FPSO
-
GDS-2209/GXS-E330
tovuti ya uso wa bomba
Hainan Huasheng
mnara wa kurejesha phenol
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Nyingine |
| GB/T KANUNI | 0.057 | 1.1 | 0.74 | 0.026 | 0.005 | 9.8 | 28.4 | 0.07 | 0.11 | - |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | THAMANI YA IMAPACT J/℃ | Matibabu ya joto °C*h | ||||
| GB/T KANUNI | 800 | 25 | - | - | ||||
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
| MAELEZO YA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| UMEME (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||