Vyuma vya pua Flux Cored Wire E347T1-1/4 LNG exp ort pipeline project weld
TEKNOLOJIA YA KUCHOMA
Usiruhusu maswali
Endelea kukusumbua
Arc kutokuwa na utulivu
Ukingo usiopendeza
Spatter nyingi
Bora intergranular ulikaji upinzani kutokana na
nyongeza ya Nb; Wote kulehemu nafasi, kulehemu kupita ni laini
Arc ni laini na imara, chini ya splash, nzuri ya kutengeneza, slag nzuri
kuondolewa, kulisha waya thabiti, na utendaji bora wa mchakato wa kulehemu.
Ripple faini
Aina ya kalsiamu ya titanium
electrode ya mkono ya chuma cha pua
Sehemu kuu ni 1 8%Cr- 9%Ni
Slagging rahisi
Bidhaa Parameter
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Nyingine |
| GB/T KANUNI | 0.02 | 0.65 | 1.40 | 0.018 | 0.003 | 9.4 | 20.2 | 0.015 | Nb:0.5 Cu:0.01 |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | Kurefusha/% | THAMANI YA IMAPACT J/℃ | Matibabu ya joto °C*h | |||||
| GB/T KANUNI | - | 665 | 40 | - | - | |||||
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
| MAELEZO YA DIAMETERS(mm) | 1.2 | 1.6 | |||
| Voltage (Volt) | 20-36 | 24-38 | |||
| Umeme (Amp) | 120-260 | 200-300 | |||
| Kasi(mm/min) | 15-25 | 18-25 | |||
| Urefu wa kunyoosha kavu (mm) | 15-25 | 15-25 |
Msaada wa kiwanda
Bidhaa hiyo inafaa kwa a
mbalimbali ya maombi
TEKNOLOJIA YA KUCHOMA
-
Vifaa vya kulehemu kwa aloi za alumini
-
tani 9,000 za kemikali
-
Uchina-Urusi mbele ya mashariki
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Nyingine |
| GB/T KANUNI | 0.02 | 0.65 | 1.40 | 0.018 | 0.003 | 9.4 | 20.2 | 0.015 | Nb:0.5 Cu:0.01 |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | Kurefusha/% | THAMANI YA IMAPACT J/℃ | Matibabu ya joto °C*h | |||||
| GB/T KANUNI | - | 665 | 40 | - | - | |||||
VIGEZO VINAVYOPENDEKEZWA VYA KUCHOMEZA:
| MAELEZO YA DIAMETERS(mm) | 1.2 | 1.6 | |||
| Voltage (Volt) | 20-36 | 24-38 | |||
| Umeme (Amp) | 120-260 | 200-300 | |||
| Kasi(mm/min) | 15-25 | 18-25 | |||
| Urefu wa kunyoosha kavu (mm) | 15-25 | 15-25 |