Aloi za nickel TIG ERNiCr-3 Vifaa vya kuuza bidhaa
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T KANUNI | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
| KANUNI ZA AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
| MFANO THAMANI | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | THAMANI YA IMAPACT J/℃ | UREFU(%) | ||||
| GB/T KANUNI | - | - | - | - | ||||
| KANUNI ZA AWS | - | - | - | - | ||||
| MFANO THAMANI | - | 710 | 170-196 | 39 | ||||
Waya ya aloi ya gesi ya nikeli-chromium-chuma nikeli-msingi ya aloi, muundo wa kawaida ni 72%Ni-20%Cr-3%Mn-2.5%Nb+Ta.
Chuma kilichounganishwa kina sifa nzuri za mitambo, upinzani mzuri wa kutu, upinzani wa juu wa oxidation na nguvu ya kutambaa.
Safu thabiti, uundaji mzuri, mtiririko mzuri wa chuma kilichoyeyuka, na utendaji bora wa mchakato wa kulehemu.
-
Uwanja wa Mafuta wa Qinghai Youjian Wunan
-
Vifaa vya kulehemu kwa chupa za gari la LNG
-
Hita yenye shinikizo la juu ya Hangzhou Boiler Group Co. LTD
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T KANUNI | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
| KANUNI ZA AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
| MFANO THAMANI | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | THAMANI YA IMAPACT J/℃ | UREFU(%) | ||||
| GB/T KANUNI | - | - | - | - | ||||
| KANUNI ZA AWS | - | - | - | - | ||||
| MFANO THAMANI | - | 710 | 170-196 | 39 | ||||