Pamoja na maendeleo ya haraka ya vifaa vya kimataifa vya kemikali na nishati, mizinga ya kuhifadhia chuma cha pua na vyombo hutumiwa sana katika usafirishaji na uhifadhi wa kemikali, chakula na vinywaji, nishati na vifaa vingine. Kwa sababu ya ugumu wake bora wa joto la chini na upinzani mzuri wa kutu, chuma cha pua cha austenitic hutumiwa sana katika ujenzi wa matangi ya kuhifadhia ya cryogenic, vifaa na miundo mikubwa ya cryogenic.
Tangi ya kuhifadhi cryogenic
2.Utangulizi mfupi wa vifaa vyetu vya kulehemu vya -196℃ vya joto la chini vinavyoathiri chuma cha pua
| Kategoria | Jina | Mfano | Kawaida | Toa maoni | |
| GB/YB | AWS | ||||
| Electrode | GES-308LT | A002 | E308L-16 | E308L-16 | -196℃≥31J |
| Flux waya | GFS-308LT | - | TS 308L-F C11 | E308LT1-1 | -196℃≥34J |
| Waya imara | GTS-308LT (TIG) | - | H022Cr21Ni10 | ER308L | -196℃≥34J |
| GMS-308LT (MIG) | - | H022Cr21Ni10 | ER308L | -196℃≥34J | |
| SAW | GWS-308/ GXS-300 | - | S F308L FB-S308L | ER308L | -196℃≥34J |
3.Elektrodi yetu GES-308LT (E308L-16)
Ili kukidhi mahitaji ya soko, kampuni yetu imetengeneza aina mbalimbali za halijoto ya chini kabisa, elektroni za chuma cha pua zenye ugumu wa hali ya juu, muundo wa kemikali wa chuma kilichowekwa (kama inavyoonyeshwa katika Jedwali 1) na sifa thabiti za mitambo (kama inavyoonyeshwa kwenye Jedwali. 2), na ina mchakato bora wa kulehemu wa nafasi zote Utendaji, na ushupavu bora wa athari ya halijoto ya chini, athari ya kiasi chake cha ferrite kwenye thamani ya athari (Jedwali 3).
1.Utungaji wa kemikali wa chuma kilichowekwa
| E308L-16 | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | N | Fn |
| NB (%) | 0.04 | 0.5-2.5 | 1.0 | 0.030 | 0.020 | 9.0-12.0 | 18.0-21.0 | 0.75 | 0.75 | - | - |
| Sampuli1 | 0.022 | 1.57 | 0.62 | 0.015 | 0.006 | 10.25 | 19.23 | 0.020 | 0.027 | 0.046 | 6.5 |
| Sampuli2 | 0.037 | 2.15 | 0.46 | 0.018 | 0.005 | 10.44 | 19.19 | 0.013 | 0.025 | 0.45 | 3.8 |
| Sampuli3 | 0.032 | 1.37 | 0.49 | 0.017 | 0.007 | 11.79 | 18.66 | 0.021 | 0.027 | 0.048 | 0.6 |
Jedwali 1
2.Mechanical mali ya chuma zilizowekwa
| E308L-16 | Mazao MPa | Tensile MPa | Kurefusha % | -196℃athari J/℃ | GB/T4334-2020 E Kutu ya kati ya punjepunje | Rukaguzi wa adiografia | Toa maoni | |
| Thamani moja | Thamani ya wastani | |||||||
| NB | - | 510 | 30 | - | - | - | I | - |
| Sampuli1 | 451 | 576 | 42 | 32/32/33 | 32.3 | waliohitimu | I | - |
| Sampuli2 | 436 | 563 | 44 | 39/41/39 | 39.7 | waliohitimu | I | - |
| Sampuli3 | 412 | 529 | 44.5 | 52/53/55 | 53.3 | waliohitimu | I | - |
Jedwali 2
3.Athari ya kiasi cha feri ya chuma iliyowekwa kwenye athari
4.Onyesho la mchakato wa kulehemu (φ3.2mm)
Kulehemu wima kabla na baada ya kuondolewa kwa slag (DC+)
Uchomeleaji wa bomba kabla na baada ya kuondolewa kwa slag (DC+)
4. Tahadhari kwa kulehemu wima
1. Ulehemu wa chini wa sasa unapaswa kutumika;
2. Weka arc chini iwezekanavyo;
3. Wakati arc inazunguka kwa pande zote mbili za groove, simama kwa muda, na upana wa swing unadhibitiwa ndani ya mara 3 ya kipenyo cha electrode.
5.Pipeline picha ya kulehemu matumizi ya matumizi
Kwa -196 ℃ vifaa vya kulehemu vya chuma cha pua vyenye athari ya joto la chini, baada ya miaka mingi ya utafiti na ukuzaji wa vifaa vya kulehemu, tayari tunayo vifaa vinavyotumika vya kulehemu vya vijiti vya kulehemu, core imara, chembechembe za mfereji na safu zilizozama, na tumetengeneza safu ya elektrodi ya mkono inayoendelea. kulehemu vifaa vya matumizi kwa kulehemu kwa nafasi zote, na ina mafanikio mengi ya maombi ya uhandisi, karibu wateja kushauriana na kuchagua!
Muda wa kutuma: Dec-16-2022