Aloi za alumini TIG ER5356 Uunganishaji wa kulehemu
COMPONET YA KIKEMIKALI:
| ALLOY(wt%) | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S |
| GB/T KANUNI | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Pembezoni |
| KANUNI ZA AWS | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Pembezoni |
| MFANO THAMANI | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Pembezoni |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | Chuma cha mzazi | UREFU(%) | Matibabu ya joto | ||||||
| GB/T KANUNI | - | - | - | - | - | ||||||
| KANUNI ZA AWS | - | - | - | - | - | ||||||
| MFANO THAMANI | 105 | 205 | 2014-0 | 17 | AW | ||||||
Sehemu kuu ni ALMg5Cr.
k5% ya utupaji wa magnesiamu na kutengeneza kulehemu kwa aloi ya alumini au uso wa uso, nyenzo za kulehemu zima, nguvu ya juu, upotevu mzuri, upinzani mzuri wa kutu.
Kulisha kwa waya laini, mwako thabiti wa safu, splash haifanyiki vizuri.
-
Vifaa vya kulehemu kwa aloi za alumini
-
Reactor ya polypropen
-
Gansu Lanke Petrochemical -50℃ mradi wa tanki ya spherical ya propane
COMPONET YA KIKEMIKALI:
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S | |
| GB/T KANUNI | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Pembezoni |
| KANUNI ZA AWS | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Pembezoni |
| MFANO THAMANI | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Pembezoni |
MALI YA MITAMBO:
| MALI | NGUVU YA MAVUNO(MPa) | NGUVU YA UPANUZI(MPa) | Chuma cha mzazi | UREFU(%) | Matibabu ya joto | ||||||
| GB/T KANUNI | - | - | - | - | - | ||||||
| KANUNI ZA AWS | - | - | - | - | - | ||||||
| MFANO THAMANI | 105 | 205 | 2014-0 | 17 | AW | ||||||